标题(中文):基于cspbx3 (x = br, i)量子点玻璃固体材料的多色发光二极管 标题(英文):multicolour light-emitting diodes based on cspbx3 (x = br, i) quantum dots glasses solid materials 刊物名称及期号、页码:materials letters, 229, 290-292 作者姓名(中文):袁荣荣,沈伶俐,刘胜男,丁玲,张慧灵,向卫东,梁晓娟 作者姓名(英文):rongrongyuan,yinzicheng,shengnanliu,lingding,huilingzhang,weidongxiang,xiaojuanliang 摘要(英文): in this paper, cspbx3 (x = br, i) quantum dots glasses solid materials are fabricated based on the melting and heat-treatment methods. a series of characterization measurements are carried out to research the microscopic morphology and luminescent properties of solid materials. finally, the multicolour light-emitting devices (leds) are constructed by adhesion commercial ingan blue chip with as-prepared glasses. 研究现状(中文): 目前,在发光二极管领域中已被报道为潜在的发射材料主要包括cdse,zns, sno2, cds, cdte, inp@znses, cuins2, cuins2 /zns和cu掺杂znins。而全无机钙钛矿cspbx3量子点由于发射窄,量子效率高,可调性好等光学性质成为了量子点发射领域的新秀材料。cspbx3 量子点在照明和激光器,偏振器,太阳能电池和光电探测器中都有很大应用潜力。尽管量子点在溶剂中具有极好的发光性能,易挥发的溶剂会导致量子点随之挥发,不仅有害人类健康,还造成了资源的浪费。此外,阴离子交换反应是也很容易发生在不同的卤素之间,会破坏钙钛矿完美晶体的结构而造成量子点发光不稳定的现象。因此,提高稳定性和减少负离子交换反应几率是当前研究的主要出发点。 为此,温州大学向卫东课题组探索了一系列多色钙钛矿固体材料—— cspbx3 量子点玻璃。硕士研究生袁荣荣等人成功的将cspbbr3、cspbbr1.5i1.5、cspbi3 量子点嵌入了zn-b-si玻璃基质中,机械稳定性优良的玻璃基质赋予了量子点更高的稳定性。同时,量子点被限制在玻璃晶格中也大大降低了离子交换反应的几率。实验表明,在蓝光激发下,三种玻璃的发光色纯度均在95%以上,表明该系列钙钛矿玻璃可以有效的吸收蓝光。
创新点(中文): 1. cspbx3 钙钛矿量子点玻璃具有良好的发光特性和稳定性。 2. cspbbr3钙钛矿量子点玻璃的最高量子效率达到42.7%。 3. 多色发光二极管波长范围:548.7-700.00 nm。 4. cspbbr3和cspbbr1.5i1.5钙钛矿量子点玻璃的纯度高达96.9%和99.9%。
原文链接:
| |||
0 | |||
|